Sustainable Grade
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). UL94 V0 and 5VA listing. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI); Steam, Gamma, EtO, and E-beam sterilizable.
This material is food contact compliant in most jurisdictions – exceptions may exist, request a declaration for details.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 1 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 2 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 4 | ≥3 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94-5VA Flame Class Rating | ≥1.9 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating | ≥0.25 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 48 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 64 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 8 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 64 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 70 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 24 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 350 - 400 | °C | |
| Nozzle Temperature | 345 - 400 | °C | |
| Front - Zone 3 Temperature | 345 - 400 | °C | |
| Middle - Zone 2 Temperature | 340 - 400 | °C | |
| Rear - Zone 1 Temperature | 330 - 400 | °C | |
| Mold Temperature | 135 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 114 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 115 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 6 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 4610 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 225 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6850 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 115 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 115 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 228 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6890 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.34 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.4 | % | SABIC method |
| Melt Flow Rate, 337°C/6.6 kgf | 11.3 | g/10 min | ASTM D1238 |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.9 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 220 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 207 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 3.0E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 5.1E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 3.0E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.1E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 220 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 213 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 170 | °C | UL 746B |