LNP LUBRICOMP RI001 compound is based on Nylon 6/6 resin containing 2% silicone. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1630 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 45 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 6 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 214 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 275 - 290 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 61 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.6 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 3200 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2910 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 68 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.7 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 4.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2930 | MPa | ISO 527 |
| Flexural Stress | 96 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2690 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.15 | - | ASTM D792 |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 1.2 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 2 - 4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 2 - 4 | % | ASTM D955 |
| Wear Factor Washer | 104 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Ring | -1 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.43 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.26 | - | ASTM D3702 Modified: Manual |
| Moisture Absorption (23°C / 50% RH) | 1.5 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 241 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 66 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 8.3E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 8.E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 164 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 59 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.03 | % | |
| Melt Temperature | 200 - 210 | °C | |
| Front - Zone 3 Temperature | 195 - 205 | °C | |
| Middle - Zone 2 Temperature | 190 - 200 | °C | |
| Rear - Zone 1 Temperature | 180 - 195 | °C | |
| Mold Temperature | 15 - 45 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 69 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 57 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 58 | % | ISO 527 |
| Flexural Stress, break, 2 mm/min | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 9.7E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.33E-04 | 1/°C | ISO 11359-2 |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |